    EPOXY RESINS

    RE 071MR

      The compound RE 071MR is a semi-flexible two components epoxy system consisting of an epoxy resin mixed with aggregate and an amino additional agent. Once it has been hardened the product features excellent mechanical and dielectric properties and good resistance to humidity. The product is used for solventless coatings to protect kernels and windings of electric transformers, industrial plants, buildings and swimming-pools. The compound hardens at a temperature higher than 10°C, and it can be manufactured in the colour black (RE071MN) and grey (RE071MG).

      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (A) red (B) colourless
      Density 25°C ASTMD 1475/60 (A) 1,520 -1,540 - (B) 1,020-1,030
      Viscosity 25 °C ASTMD 2393/80 (A) 11.000-19.000 mPa.s (B) 250-500 mPa.s
      Water absorption ASTMD 3418 0,1%
      Dielectric resistance ASTMD 149/61 12 KV/mm
      Volume resistivity ASTMD 257/61 1012 Ohm


    RE 102
      The resin RE 102 is an average viscosity product formulated with epoxy resins with the property to harden for the action of a catalyst.
      The reaction, that causes the hardening, happens to high temperature and it is as more rapid as higher is the temperature.
      This resin, thanks to tridimensional reticular property, features a considerable dimensional stability and thermic ageing resistance and it has been designed and set up for the motors treatment with drop by drop system.
      The resin, when warm, becomes very fluid and enters easily in the windings impregnating them completely and uniformly.
      It has very good compatibility with each kind of enamelled wire.

      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (Transparent straw-yellow
      Density 25°C ASTMD 1475/60 (1,100 - 1,170
      Viscosity 25 °C ASTMD 2393/80 1.200 - 3.200 mPa.s
      Water absorption ASTMD 3418 0,15%
      Dielectric resistance ASTMD 149/61 14 KV/mm


    RE 110
      The resin RE 110 is a low viscosity product formulated with synthetic and epoxy resins with the property to harden for the action of a catalyst.
      The reaction, that causes the hardening, happens to high temperature and it is more rapid as higher is the temperature.
      The resin, thanks to tridimensional reticular property, features a considerable dimensional stability and a thermic ageing resistance.
      It has been specifically designed for the motors treatment with drop by drop system.
      The resin, when warm, becomes very fluid and enters easily in the windings impregnating them completely and uniformly.
      It has very good compatibility with each kind of enamelled wire.

      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (Transparent straw-yellow
      Density 25°C ASTMD 1475/60 1,130 - 1,170
      Viscosity 25 °C ASTMD 2393/80 1.000 - 1.800 mPa.s
      Water absorption ASTMD 3418 0,15%
      Dielectric resistance ASTMD 149/61 14 KV/mm


    RE 203
      The compound RE203 is a two components epoxy system, without solvents: a modified epoxy resin and a modified aliphatic amine adduct to low harmfulness.
      The system polymerizes at room temperature forming a bright film not sticky also in humidity presence. Once it has been polymerized the system features: very good electric and mechanical properties, excellent resistance to humidity and atmospheric agents, good temperature resistance (F insulation class).
      It is used for magnetic coils and windings of transformers and industrial plants.
      It can be used whether brush or airless spray.

      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (A) straw-yellow (B) colourless
      Density 25°C ASTMD 1475/60 (A) 1,090 - 1,110 (B) 1,050-1,080
      Viscosity 25 °C ASTMD 2393/80 (A) 10.000 - 12.000 mPa.s (B) M-R
      Water absorption ASTMD 3418 0,02% - 0,03%
      Dielectric resistance ASTMD 149/61 10 - 12 KV/mm
      Volume resistivity ASTMD 257/61 6x1015- 7,8x1015Ohm


    RE 305PM
      The resin RE 305PM is made with modified epoxy resins opportunely charged to give a pasty consistence and a thixotropy suitable to smearing and not adhesive.
      It has a great resistance to chemical and physical agent, a good thermal conductivity and excellent electric properties. It is compatible with all kinds of enamelled wire.
      It is suitable for equipments that have to work in F insulation class.
      It can be supply also in black colour.


      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (A) brilliant red (B) colourless
      Density 25°C ASTMD 1475/60 (A) 1,120- 1,160 (B) 1,050-1,080
      Viscosity 25 °C ASTMD 2393/80 (A) 20.000-30.000 mPa.s (B) 250-500 mPa.s
      Water absorption ASTMD 3418 0,3%
      Dielectric resistance ASTMD 149/61 16 KV/mm
      Volume resistivity ASTMD 257/61 713 Ohm


    RE 310
      The resin RE 310 is made with epoxy resins and special bitumes. It has been specifically designed for the insulation of electric cable joint.
      It has an excellent flexibility that together with thermic stability, low retiring after the polymerization and rapid hardening, render the product a necessary and technically advanced instrument.
      Furthermore it has an excellent chemical agent and water resistance.
      It is suitable for tension till 10 KV and for little joints of capacity till KG 0,400.


      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (A) yellow (B) colourless
      Density 25°C ASTMD 1475/60 (A) 1,450-1,550 - (B) 1,630-1,185
      Viscosity 25 °C ASTMD 2393/80 (A) 5.000-8.000 mPa.s - (B) 1.500-3.000 mPa.s
      Water absorption ASTMD 3418 0,12%
      Dielectric resistance ASTMD 149/61 21 KV/mm
      Volume resistivity ASTMD 257/61 3,913 Ohm


    RE 385
      The resin RE 385 is made with liquid epoxy resins designed to permit a easy penetration in the objects to impregnate.
      It is a product of high technology suitable to varied applications when a great chemical and mechanical agents resistance and a strong adhesiveness is requested.
      It can be strongly charged with considerable saving cost.
      It features a smooth and bright surface.


      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (A) pale yellow (B) colourless
      Density 25°C ASTMD 1475/60 (A) 1,120- 1,160 - (B) 1,050-1,080
      Viscosity 25 °C ASTMD 2393/80 (A) 900-1.000 mPa.s - (B) 250-500 mPa.s
      Water absorption ASTMD 3418 0,2%
      Dielectric resistance ASTMD 149/61 21 KV/mm
      Volume resistivity ASTMD 257/61 8,512 Ohm


    RE 390
      The resin RE 390 is made with modified epoxy resins specifically designed for electrotechnic and electronic industry.
      Also if it is completely reactive it has an excellent flessibility that together with the high chemical, mechanical and electrical resistance, give to the resin those peculiarity of product highly qualified and versatile.
      It is compatible with all kinds of enamelled wire and suitable for equipments that work in B and F insulation class.


      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (A) light yellow (B) colourless
      Density 25°C ASTMD 1475/60 (A) 1,090- 1,110 - (B) 1,050-1,080
      Viscosity 25 °C ASTMD 2393/80 (A) 9.500-12.000 mPa.s - (B) 250-500 mPa.s
      Water absorption ASTMD 3418 0,15%
      Dielectric resistance ASTMD 149/61 22 KV/mm
      Volume resistivity ASTMD 257/61 813 Ohm


    RE 925
      The resin RE 925 is an epoxy compound, without solvent formulated to obtain a product that once it has been polymerized it features very good electric properties, thermal conductivity and excellent resistance to the stress of chemical and physical nature and of thermal shock. With hardening, after the mixing of the two components, smooth and bright surface is obtained.
      It is compatible with all kinds of enamelled wire. The polimeryzed resin has a high humidity resistance.
      It is suitable for the production of equipments that work in F insulation class and in particular for the encapsulation of electromagnetic brakes.


      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (A) black (B) amber
      Density 25°C ASTMD 1475/60 (A) 1,700- 1,800 - (B) 0,980-1,000
      Viscosity 25 °C ASTMD 2393/80 (A) 9.500-12.000 mPa.s - (B) 600-1.000 mPa.s
      Water absorption ASTMD 3418 0,18%
      Dielectric resistance ASTMD 149/61 18 KV/mm
      Volume resistivity ASTMD 257/61 1013 Ohm


    RE 5211
      The resin RE 5211 is a modified epoxy resin with addition of particular powders in order to give very good electric properties, good thermal conductivity combined with low viscosity and with an excellent resistance to stresses of chemical and physical nature.
      The hardening, after the two components mixing, happens to room temperature superior to 10°C and causes smooth and bright surface also in presence of high environmental humidity.
      The resin is compatible with all kinds of enamelled wire and once it has been hardened the product features very good electrical properties.
      It is suitable for the production of equipments that have to work in F insulation class.


      C H A R A C T E R I S T I C S
      STANDARDS VALUE
      Colours - (A) rosso - (B) avorio
      Density 25°C ASTMD 1475/60 (A) 1,350- 1,450 - (B) 1,170-1,200
      Viscosity 25 °C ASTMD 2393/80 (A) 2.000-3.000 mPa.s - (B) 500-800 mPa.s
      Water absorption ASTMD 3418 0,15%
      Dielectric resistance ASTMD 149/61 18 KV/mm
      Volume resistivity ASTMD 257/61 1014 Ohm


    The epoxy resins here shortly described represent a minimum part of our production. For further technical information and/or specific requests you can contact us to the following address

    Notes: The information given in this data sheet are the results of careful researches and several tests carried out in our laboratory. Because of the various and particular applications, these information are merely indicative without our responsibility.
 




ANGI srl manufacture and trade of electric insulating materials
angi@angisrl.com
Administration office
20127 Milano
viale Brianza, 8
telefono 02.26144247
fax 02.2893746		Commercial offices and warehouse
14018 Villafranca d'Asti
loc. Case Bruciate, 37
telefono 0141.943825
fax 0141.943170